Heating motor Objective Heat steel to help bond an injection molded piece and help the reflow.Material Steel motor body, 60 x 60 x 27 (2.4 x 2.4 x 1.1) mm(in)Temperature 260C (500F)Frequency 237 kHzEquipment • Power of 20kW induction heating system, equip…

Date：2008/08/03

Heating steel rivets Objective Heating steel rivets prior to head formingMaterial steelTemperature 1292 F (700C)Frequency 83 kHzEquipment • Power of 7 kW induction heating system, equipped with a remote workhead containing one 1.5μF capacitor.• An induc…

Date：2008/08/03

Heating engine head Objective Heat steel liners on the head of an engine to remove aluminium casing. Material Steel, 80 mm ID x 190 mm (3.1 in x 7.5 in.) Temperature 650 C (1202 F) Frequency 81 kHz Equipment Power of 35kW induction heating system, …

Date：2008/08/03

Heating aluminium susceptor Objective Expand powder into solid form for use in crash helmetsMaterial Microspheric powderAluminium chamber 110mm (4.3 in.) diameter x 35mm (1.3 in.) deep used to hold powderTemperature 150 oC (302 oF)Frequency 54.5 kHzProcess…

Date：2008/08/03

Heating Titanium Blade Objective Heat a titanium blade to 500F (200C) to melt and drain the wax from inside the blade.Material 4” length (101.6mm) titanium blades with 1.5” x 0.25” (38.1mm x 6.4mm) metering areaTemperature 500F (200C)Frequency 186 kHzEq…

Date：2008/08/03

Heating Engine Valve Objective To heat the face of an engine valve head to 900F and maintain the temperature for an extended time, hightemperature stress test.Material Engine valve head (two sizes), temperature sensing paintTemperature 900 FFrequency 223 k…

Date：2008/08/03

Pre-heating Truck Axle Objective To pre-heat the seam of a truck axle to over 300F within 15 seconds for a welding application and maintain temperature within the welding zone for 15 seconds after the power isturned off.Material Steel truck axle; 350 and 4…

Date：2008/08/03

Heating Eight Steel Rods Objective Heat eight steel rods simultaneously to 212F (100C) for a molding operation.Material 8 Steel Rods measuring 1/2 (12.7mm) in diameter and 14 (355.6mm) long held in place by 2.5” (63.5mm) diameter Teflon end plates.Tempera…

Date：2008/08/03

Melting Furnaces Characteristics of cast iron to a large extent depend on the content of harmful impurities and, above all, of sulfur. For modifications to the high-strength nodular cast iron should have a low sulfur content. In cupola furnaces to smel…

Date：2008/08/03

Heat treating process Heat treating is an essential phenomenon that is very much needed to manipulate the physical, as well as sometimes the chemical properties of a metal. Though it finds its application in the metallurgical process, heat treating is also…

Date：2008/08/03