Induction Hardening Steel
Views Send Enquiry
Objective To harden various size ends of hand held marking stamps. The area to be hardened is 3/4” (19mm) up the shank.
Material Steel stamps 1/4” (6.3mm), 3/8” (9.5mm), 1/2” (12.7mm) and 5/8” (15.8mm) square
Temperature 1550 ºF (843 ºC)
Frequency 99 kHz
Equipment • Power of 45kW induction heating system, equipped with a remote workhead containing eight 1.0μF capacitors for a total of 2.0μF
• An induction heating coil designed and developed specifically for this application.
Process A two turn channel coil is used to cover the range of steel stamps being heated. The 5/8” steel stamp is heated for 60 seconds to reach 1550 ºF (843 ºC) and the desired hardness.
Smaller parts will also heat easily.
Results/Benefits Induction heating provides:
• Faster process time and production rates
• Hands-free heating that involves no operator skill for manufacturing
• Controlled precise application of heat
hardening-steel
Related Content
Air Cooled clamp coil (half-open coil) for preheating gas pipeline
induction coating by air cooled clamp induction coil
Remove plastic coating from steel tubes by Induction Heating
Releasing Fixture by Induction Heating
U shape air cooled induction coil by UM-100C-HF for pipeline preheating
induction quenching with custom-design inductor
induction brazing diamond segment
induction brass soldering copper plate_2
Hot
induction hardening axle (shaft) by 100KW induction heater
induction quenching axle (shaft) by 160KW induction heater
induction hardening inner surface (inwall)
Induction Hardening Harvestor Combined Finger
Induction Hardening Harvestor Combined Blade
workpiece for induction hardening
induction hardening veterinary instrument
induction hardening surgical device
Newest Comment
No Comment
Post Comment