parts of fully automatic induction machine

2010/04/30

Annealing is a heat treatment in which material is exposed to an elevated temperature and slowly cooled. Annealing of the material changes physical properties of the material such as strength and hardness.UIHM ​induction annealing machines are designe

2009/10/02

STRESS RELIEVING,NORMALISING AND ANNEALINGStress RelievingStress relieving is applied to both ferrous and non-ferrous alloys and is intended to remove internal residual stresses generated by prior manufacturing processes such as machining, cold rolling an

2007/04/03

Objective To heat steel tubes to 2000 F (1093 C) in an inert atmosphereMaterial 0.1” (2.54mm) diameter stainless steel tubeTemperature 2000 FFrequency 333 kHzEquipment • 10 kW induction heating system, equipped with a remote workhead containing one 1.0μ…

2006/10/02

Objective Annealing the end of a steel hydraulic motor shaft prior to machiningMaterial .75” (19mm) diameter steel rod, 6” (152.4mm) long with a keyway at the endTemperature 1350 F (732 C)Frequency 359 kHzEquipment • UM-06A-UHF induction heating system,…

2006/10/02

Objective Annealing aluminum fuel tank fill neck to 650 F (343 C)Material Aluminum fill neck 2.5” (63.5mm) diameter, 14” (35.5cm) longTemperature 650 F (343 C)Frequency 85 kHzEquipment • 40kW induction heating system, equipped with a remote workhead con…

2006/10/02

Objective Continuously anneal a brass wire used in electric motors at a rate of 16.4 yds (15m) per minute to eliminate work hardening caused during the drawing process.Material Square copper wire 0.06” (1.7mm) dia., temperature indicating paintTemperature

2006/10/02

Objective Annealing a 1” lip on aluminum cryogenic dewar that has been work hardened during the process of spin forming.Material Aluminum dewar, lip has a 3.24” (82.3mm) ID and is 0.05” (1.3mm) thickTemperature 800 F (427 C)Frequency 303 kHzEquipment •…

2006/10/02

Objective To heat 3” (76.2mm) from the end of the wire on a woven wire cloth 60” (1.52m) long. This prepares the wire mesh for bending in a press brake.Material Woven wire cloth (steel) made of 1/2” (12.7) diameter wire, 60” (1.52m) long. Wires are 1.5…

2006/10/02

Objective To heat both ends of a copper tube to anneal as soft as possible 1.5” (38.1mm) from end and retain full hardness next to annealMaterial 1.625” (41.275mm) dia x 24” (609.6mm) long copper tubeTemperature 1500 F (815.5 C)Frequency 70 kHzEquipment…

2006/10/02