Objective To harden various size ends of hand held marking stamps. The area to be hardened is 3/4” (19mm) up the shank.
Material Steel stamps 1/4” (6.3mm), 3/8” (9.5mm), 1/2” (12.7mm) and 5/8” (15.8mm) square
Temperature 1550 ºF (843 ºC)
Frequency 99 kHz
Equipment • Power of 45kW induction heating system, equipped with a remote workhead containing eight 1.0μF capacitors for a total of 2.0μF
• An induction heating coil designed and developed specifically for this application.
Process A two turn channel coil is used to cover the range of steel stamps being heated. The 5/8” steel stamp is heated for 60 seconds to reach 1550 ºF (843 ºC) and the desired hardness.
Smaller parts will also heat easily.
Results/Benefits Induction heating provides:
• Faster process time and production rates
• Hands-free heating that involves no operator skill for manufacturing
• Controlled precise application of heat
hardening-steel
Related Content
induction brazing SS steel by handheld induction coil
induction melting silicon and steel
magnesium oxide acidic furnace for induction melting glass
induction preheating gas pipeline by full air cooled clamp induction coil and DSP induction heater
induction melting with Titanium alloy pot by customized induction coil
induction melting aluminium for casting wire wheel
induction heating steel plate by pancake induction coil
induction heating steel knife
Hot
induction hardening surface of steel plate
induction hardening gear surface
induction hardening wheel gears
induction hardening TCT knife (tungsten carbide tool)
induction hardening knife edge (sickle blade)
induction hardening inner surface of steel pipe
induction hardening inner surface of steel ring by UHF induction heater
induction hardening inner surface of gear
Newest Comment
No Comment
Post Comment